Rubber composition and goods

ABSTRACT

A new rubber composition for use in clothing and fashion accessories, is provided. The new rubber composition includes 30-70% by weight devulcanized, recycled rubber, and most preferably, devulcanized, recycled tire rubber.

BACKGROUND OF THE INVENTION

This invention relates generally to a new and improved rubbercomposition that includes a substantial amount of devulcanized, recycledtire rubber for use in making clothing and fashion accessories andincludes a method for using the novel rubber composition to makeclothing and fashion accessories.

Billions of pounds of rubber are used every year in the United States.The largest single end use for rubber is automobile tires. After arubber tire has reached the end of its useful life, the tire is mostoften discarded to a dump or landfill. In fact, there are landfill sitesthat are full of millions of tires from previous consumption. These tirepiles create several hazards. They are breeding grounds for rats, bugs,such as mosquitoes which carry encephalitis, and other vermin. In someareas, old tires are burned for energy. However, this pollutes theenvironment and there is not a cost effective method for cleaning. Also,tire piles have been known to catch on fire and often can burn andsmolder for weeks thereby polluting the environment and creating ahealth hazard to surrounding communities.

While rubber clothing and fashion accessories have been around forseveral years, they have not been made from devulcanized, recycledrubber, and in particular, devulcanized, recycled tire rubber, or byusing the method of this invention.

SUMMARY OF THE INVENTION

It is a principal objective of the present invention to provide a rubbercomposition that is made from substantially devulcanized, recycledrubber and can be used to make clothing and fashion accessories.

It is a further object of this invention to provide a recycled rubbercomposition that is durable and retains its shape, and is made fromsubstantially devulcanized, recycled rubber.

It is a further object of this invention to provide a recycled rubbercomposition that is made from substantially devulcanized, recycled tirerubber.

It is a further object of this invention to provide a method for usingthe rubber composition to produce clothing and fashion accessories.

It is a further object of this invention to provide a use for old tirerubber that does not pollute the environment and helps to eliminate thehazards of used tire piles.

These and other features and advantages of the present invention will befurther understood upon consideration of the following detaileddescription of the invention.

BRIEF DESCRIPTION OF THE DRAWINGS

FIGS. 1a-1 i show examples of different articles of clothing that can bemade from the novel rubber composition.

FIGS. 2a-2 n show examples of different fashion accessories that can bemade from the novel rubber composition.

DETAILED DESCRIPTION OF THE PRESENTLY PREFERRED EMBODIMENT

In accordance with an embodiment of the present invention, a typicalexample of the rubber composition has about 30-70% by weight recycled,devulcanized rubber, and the remainder of the composition includesnatural or synthetic rubber, carbon black, process oil, silica,activators, process aids, accelerators and sulfur. The devulcanized,recycled rubber is preferably recycled tire rubber. The recycled tirerubber is preferably DE-VULC. DE-VULC is available from STI-K Polymersof America.

A typical embodiment of the invention has the following basecomposition, in weight percent:

Natural Rubber: 0.230 Carbon Black: 0.092 Process Oil: 0.048 Silica:0.039 Activators: 0.014 Process Aids: 0.018 Accelerators: 0.016 Sulfur:0.005 Recycled Rubber: 0.538.

The composition is mixed and rolled into a sheet form using conventionalprocessing equipment and parameters. The composition is then vulcanizedusing conventional processing equipment and parameters. Vulcanizationtransforms the rubber from a weak thermoplastic mass without usefulmechanical properties into a strong, elastic, tough rubber.Vulcanization is accomplished by applying heat and pressure to therubber composition, or it can be accomplished without heat by theaddition of chemicals such as sulfur chloride. After vulcanization, therubber composition has a tensile strength of approximately 2000-2350psi, an elongation of 325-425%, and a Shore A hardness of 45-75. Thiscombination of properties results in a particularly comfortable anddesirable feeling rubber composition. The material is particularlysuitable when the tensile strength is 2185, the elongation is 377% andthe Shore A hardness is 60.

At this point, the rubber is in sheet form and is ready to be cut orpatterned into a desired shape. For example, the rubber can be patternedfor clothing or fashion accessories. With reference to FIGS. 1a-1 i,respectively, the rubber composition is particularly suitable forclothing such as coats, jackets, pants, shirts, skirts, vests, hats,gloves and shoes. Further, with reference to FIGS. 2a-2 n, respectively,the rubber composition is particularly suitable for fashion accessoriessuch as purses, wallets, belts, luggage, portfolios, briefcases,backpacks, datebooks/address books, carrying bags, fanny packs, make-upcases, shaving kits, beach bags, and watch bands. The above list ofclothing and fashion accessories are only examples of the type ofclothing and fashion accessories that the rubber composition is usefulfor, and is not meant to limit the claims of this patent in any way.Similarly, the particular embodiments disclosed in FIGS. 1 and 2 areonly examples of the type of clothing and fashion accessories that therubber composition is useful for, and is not meant to limit the claimsof this patent in any way.

After patterning, the pieces of rubber are ready to be secured into theshape of the final desired product. For example, the rubber pieces canbe secured by sewing, riveting, tacking, or gluing. Other procedures forsecuring the rubber are also available.

The foregoing detailed description has been given for clearness ofunderstanding only, and no unnecessary limitations should be understoodtherefrom, as modifications will be obvious to those skilled in the art.

What is claimed is:
 1. A final, vulcanized rubber composition, that isnot a thermoplastic, for use in making clothing and fashion accessorieshaving a tensile strength of 2000-2350 psi, and elongation of 325-425%,and a Shore A hardness of 45-75 and comprising, before vulcanization ofsaid rubber composition, about 30%-70% (by weight) devulcanized,recycled rubber.
 2. The rubber composition of claim 1 wherein saiddevulcanized, recycled rubber comprises substantially recycled tires. 3.The rubber composition of claim 2 wherein said rubber compositionfurther comprises natural or synthetic rubber, carbon black, processoil, silica, activators, process aids, accelerators and sulfur.
 4. Amethod for using a final, vulcanized rubber composition, that is not athermoplastic, to make clothing and fashion accessories comprising thesteps of: providing a rubber composition consisting essentially of,about 30-70% devulcanized, recycled rubber by weight, and the remaindercomprising natural or synthetic rubber, carbon black, process oil,silica, activators, process aids, accelerators and sulfur; sheeting saidrubber composition; vulcanizing said rubber composition; cutting saidrubber composition after vulcanizing; and securing the rubbercomposition.
 5. The method of claim 4 wherein said rubber compositionhas a tensile strength of 2000-2350 psi, an elongation of 325-425%, anda Shore A hardness of 45-75.
 6. The method of claim 5 wherein saiddevulcanized, recycled rubber comprises substantially recycled tires. 7.The method of claim 6 wherein said securing comprises sewing.
 8. Themethod of claim 6 wherein said securing comprises riveting.
 9. Themethod of claim 6 wherein said securing comprises tacking.
 10. Themethod of claim 6 wherein said securing comprises gluing.
 11. A personalarticle comprising a final, vulcanized rubber composition, that is not athermoplastic. said rubber composition before vulcanization consistingessentially of about 30-70% devulcanized, recycled rubber by weight, andthe remainder comprising natural or synthetic rubber, carbon black,process oil, silica, activators, process aids, accelerators and sulfur.12. The personal article of claim 11 wherein said rubber composition hasa tensile strength of 2000-2350 psi, an elongation of 325-425%, and aShore A hardness of 45-75.
 13. The personal article of claim 12 whereinsaid devulcanized, recycled rubber comprises substantially recycledtires.
 14. The personal article of claim 13 wherein said personalarticle is a fashion accessory.
 15. The personal article of claim 14wherein said fashion accessory is a purse.
 16. The personal article ofclaim 14 wherein said fashion accessory is a wallet.
 17. The personalarticle of claim 14 wherein said fashion accessory is a belt.
 18. Thepersonal article of claim 14 wherein said fashion accessory is luggage.19. The personal article of claim 14 wherein said fashion accessory is aportfolio.
 20. The personal article of claim 14 wherein said fashionaccessory is a briefcase.
 21. The personal article of claim 14 whereinsaid fashion accessory is a backpack.
 22. The personal article of claim14 wherein said fashion accessory is a datebook/address book.
 23. Thepersonal article of claim 14 wherein said fashion accessory is acarrying bag.
 24. The personal article of claim 13 wherein said personalarticle is clothing.